Automatic thermal film lamination machine

Process of Automatic thermal film lamination machine

1.Firstly, the thermoplastic resin is heated to temperature above the melting point.

2.The molten plastics are pushed through an extrusion die to form a thin hot film that will then be laminated over a kind of base material which has been pre-coated.

The resultant laminate is totally odorless.

Plastic resins that can be used on our extrusion lamination equipment include the LDPE, LLDPE, EVA, EAA, and other laminating resin.

The substrate wound onto the primary unwinding roller is usually BOPP (15-60um) or BOPET (12-50um). 

Applications 
Paper: Kraft paper., air-laid paper, and cardboard lamination to produce book packaging, snack packaging, duct tape for trash bag 
BOPP, BOPET, BOPA, and other plastic film lamination 
Non-woven fabric lamination, PE, PP stretch film extrusion lamination 
Aluminum foil and PE stretch film lamination 

Technical Specifications of Automatic thermal film lamination machine
Laminating Width: 800~1500mm
Maximum Mechanical Speed of the extrusion lamination line: 150m/min
Extruder: HL-90 or HL-100
Extruder Motor: 47~75kw
Maximum Extrusion Output: 260kg/h
Resin: LDPE, PP, EVA, EAA, LLDPE, EMA, EMAA, and other laminating resin (mainly 
EVA)
Coating Thickness: 8~30μm
Thickness Uniformity: ≤±5%
Maximum Diameter of Unwound Roll: 800mm

Substrate: BOPP, BOPET, BOPA, CPE, CPP, thin paper (50~200g/m2)
Coating and Drying: Gloss roller, floor-standing or horizontal drying oven
Maximum Diameter of Unwound Roll: 800mm
Tension Control: Automatic tension control 
Extrusion Lamination Line Control Method: Imported PLC system, human-machine interface 
Variable Frequency Drive: Imported AC digital vector control (variable frequency drive)