INDUSTRIAL EPOXY ZINC CHROMATE PRIMER PAINT FOR METAL STEEL

PRODUCT NUMBER

No. 1008

TYPE

A two-pack, anti-corrosive paint based on Epoxy Resin with zinc chromate pigment.

USES

Anti-corrosive under coat for weathering steel parts above water line and exteriors of tanks, factories and coastal facilities.  

CHARACTERISTICS

1.  Tough and hard film with very good adhesion.

2.  Excellent resistance to sea water.

3.  Very good resistance to oil and mild chemicals

4.  Excellent resistance to mechanical damage. 

FINISH

Flat

COLOR

Yellow 

SPECIFIC GRAVITY

Above 1.35 kg/L (Mixture)

VISCOSITY (25℃)

70 ~ 85 KU (Mixture)

DRYING TIME(25℃)

Set-to-touch 1.5 hr

Dry Hard 6 hr

Fully Cured 7 days

OVERCOATING INTERVALS

min. 8 hrs.      

OPTIMUM FILM THICKNESS

Wet 90 Microns

Dry  45 Microns   

VOLUME SOLIDS

Above 65% (Mixture)

THEORETICAL COVERAGE

11.1 meter square/L 

8.2 meter square /KG

42 meter square /GL 

THINNER

SP-12 Epoxy Thinner 

THINNING RATE

0 ~ 5 %(by wt.)

PRECEDING COATS

No.908 Wash Primer

No.1006 Epoxy Zinc Rich Primer

No.1007 Epoxy Red Lead Primer

SUBSEQUENT COATS

Topcoats of Epoxy, Vinyl, Polyurethane or Chlorinated Rubber system.

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

NOTE

1. Mix base and hardener according to the mixing ratio and stir  thoroughly.

2. Remove any soap, dut , rust , grease, old paint surface or any 

salt-containing chemicals before coating.

3. Avoid applying the paint in rainy weather or humidity above 85% RH, particularly, a wet surface must be thoroughly dried.

4. All equipment must be cleaned immediately after use.

5. When used inside tanks, sufficient ventilation must be provided.