CADMIUM-BEARING SILVER BASED SOLDER ROD MANUFACTURER

Specifications

1.A cadmium-bearing silver brazing alloy
2.High melting point and wide melting range.

 

CADMIUM-BEARING SILVER BASED SOLDER ROD

Nominal composition (weight %):HZ-Ag17C

Ag: 17

Cu: 41

Zn: 26

Cd: 16

 

Physical characteristics

Melting range (Solidus – Liquidus): 620 – 760 °C

Brazing temperature: 770 °C

Density: 8.7 g/cm3

Tensile Strength: 42 kg / mm2

 

Range of application:

HZ-Ag17C is a cadmium-bearing silver brazing alloy, with high melting point and wide melting range.

It can be used to join ferrous, non ferrous and dissimilar metals and alloys, such as steel, copper, copper alloys.

Due to its wide melting range, it can be used with good results when joint clearances are large and/or not uniform.

With this alloy particular care must be taken to keep brazing cycles as short as possible, in order to avoid possible Zinc volatilization, which will result in porosity and/or voids in the joint fillet.

When brazing in an oxidizing environment a proper flux should be used.

Due to the content of Cadmium special safety precautions must be followed during brazing operations (e.g., avoid of overheating, use of mechanical ventilation, wear of respiratory masks).

 

Characteristics Make-up:

Rods: Ø 0.5-4.0 mm 

       Length: 500 / 1.000 mm

Wires: Ø 0.3-3.5 mm (spooled and coiled)

Rings: Preforms from Wire

Pastes & Powders

Other dimensions are available upon request