manufacturer high quality stainless steel forged turnbucke

Thank you for you to pay atention to my product ,If you want to know more about ,pls see under ;If you have any reuqires ,pls without hesitate contact me 

manufacturer high quality stainless steel forgetd turnbucke 

1.Rigid quality inspecting to ensure good products.

2. Surface treating: Galvanizing & Power Coating & Painting.

3. Precise dimension size can be guaranteed during processing.

4. Most skilled professionals in charge of welding to make sure a perfect sealing.

5. Careful and cautious polishing to guarantee a clean and smooth surface.

6. Competitive price is always available.

7. SGS or BV testing are always welcomed to make ease of your mind

The fittings shall be delivered hot dip galvanized according to the following specifications:

• The Zinc that shall be used shall have the quality of minimum category prime western according to  the category Zn 98.5 according to ISO-1461.
• Then washed out with water and then flux treated and dried out.
• The hot dip galvanization shall be made in a Zinc bath of temperature 450°C and of Zn-composition min. 98,5%.
• The galvanization thickness shall be in average 86μm thick! On an isolated piece or on a small part of the surface the thickness can be a little lower, however on all pieces and on all surfaces the minimum thickness shall be 78μm and the average weight in relation to the galvanized area shall be 610 gr/m2.
• The pieces shall be after HDG free from black stains, enclosures of dirt, knobs, bubbles or any other surface defects. The HDG shall be smooth and uniform in the entire piece without any spots with too small or too big galvanization thickness otherwise the pieces will be rejected.
• The galvanization shall stick very well on the steel structure; it shall not be removed as a film but shall be as one with the steel body