Polyurethane for discontinue panels blend with polymeric mdi

Specifications

Blend polyether polyols, HCFC-141B foam agant, used for continuous panels

DBC-402B panels is a blend polyether polyols, surfactants, catalysts, foaming agent and flame retardant in a special ratio.

 

1.good flowability in the reactivity process, the foam density distributes uniformity, with excellent dimensional stability and cohesiveness.

et different requirements of continuous sandwich board product lines

 

This is one of our customer use DBC-402B.

 

Physical Properties

Appearance                       pale yellow transparent viscous liquid

Hydroxyl Value mgKOH/g                            320-400 

Dynamic Viscosity (25 °C) mPa.s             250-350

Gravity (20 °C ) g/ml                                    1.10-1.16

Storage Temperature °C                             10-25

Storage Stability month                                   6

Recommended Ratio                                  pbw 
DJD-103 blend polyols                                100

Isocyanate                                                  100-105

 

Technology and Reactivity (the exact value varied depending on processing conditions)

                                                                 Manual Mixing          Mechanical Foaming 

Raw material Temperature °C                20-25                              20-25

Mold Temperature °C                                35-45                             35-45 

Cream time s                                             30-50                               20-30

Gel time s                                                   120-200                         70-150   

Free Density kg/m3                                   23-26                              23-26

 

Foam Performance

Molding  density                                              GB/T 6343          ≥38kg/m3

Closed-cell Rate                                            GB/T 10799        ≥90%

Thermal Conductivity (15 °C)                       GB/T 3399          ≤22 mW/(m.K)

Compressive strength                                   GB/T 8813          ≥140kPa

(perpendicular to the direction of rising)            

Dimensional Stability                                    GB/T 8811      

(24h, -20 °C)                                                                                  ≤1.0% 

(24h, 100 °C)                                                                                 ≤1.5%

Flame retardant grade                                   GB/T 8624           Level  B2

 

 