(L-TYPE)MADE IN TAIWAN HIGH QUALITY SPRAY PAINT FOR CNC MACHINE

POLYURETHANE COATING (L-TYPE)

TYPE

Two-pack, based on Saturated fatty acid resin and Polyisocyanate Hardener with special pigments.

USES

Top coat for steel structure for machine and wood product, office furniture.

CHARACTERISTICS

1. High gloss with excellent appearance.

2. Excellent hardness, adhesion and abrasion resistance.

APPLICATION METHOD

Airless Spray, Roller, Brush.

COLOR

Desired colors

FINISH

High Glossy

SPECIFIC GRAVITY

Above 1 kg/L (Mixture)

VISCOSITY (25°C)

65 ~80 KU (Mixture)

DRYING TIME (25°C)

Set-to-touch

Dry hard

2 hr.

8 hrs.

OVERCOATING INTERVALS (25°C)

Min.

Max.

15 hrs.

5 days.

FILM THICKNESS

Wet

Dry

70 ~100 microns

30 ~50 microns

SOLIDS (by Weight)

Above 50%

THINNER

PU Thinner

THINNING RATE

10 ~25 %(by wt.)

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

MIXING RATIO

Base: Hardener = 3 : 1 (by volume.)

POT LIFE

4 hrs. (Mixture) (25°C)

NOTE

1. Mix base and hardener according to the mixing ratio

    and stir thoroughly.

2. Moisture, grease, rust, dirt and loose paints film on

    substrate must be removed, so are the corrosive salt

    particles. As a result, paint performance can be

    ensured.

3. Hardener must be tightly closed to avoid reaction

    with moisture in air toform bubbles and gelation.

4. Attention to the pot life.

5. Strictly controlling application, not to exceed 50 μ

    per coat,to avoid bubble formation.

6. All equipment must be cleaned immediately after

    use.