standing metal balls with base 6mm-1000mm

Specifications

all size good quality standing metal balls with base 6mm-1000mm

Physical capability of stainless steel balls
CAPABILTY MODEL	201	302	304	316
Tensile strength	100,000 - 180,000 psi	100,000-180,000 psi	100,000 - 180,000 psi	90,000 psi
Yield strength	50,000 - 150,000 psi	50,000-150,000 psi	50,000 - 150,000 psi	45,000 psi
Tensibility	55-60%	55-60%	55 - 60%	35%
Modulus of Elasticity	29,000,000 psi	29,000,000 psi	29,000,000 psi	28,000,000 psi
Density	280lbs/cubic inch	286lbs/cubic inch	286 lbs/cubic inch	290lbs/cubic inch

 

 

Chymic component of 304 stainless steel balls
CS MODEL	201	302	304	316
C	0.15% max	0.15% max	0.08% max	0.08% max
Si	1.00% max	1.00% max	1.00% max	1.00% max
Mn	5.50-7.50%	2.00% max	2.00% max	2.00% max
P	0.045% max	0.045% max	0.045% max	0.045% max
S	0.03% max	0.03% max	0.030% max	0.03% max
Cr	16.00-18.00%	17.00-19.00%	17.00- 19.00%	16.00-18.00%
Molybdenum	-----	-----	-----	2.00-3.00%
Ni	3.50-5.50%	8.00-10.00%	8.00 --10.00%	10.00-14.00%
N	-----	-----	-----	0.10% max
Nitrogen	0.25% max	-----	-----	-----

 

 

 

 

Grade 304 is the standard "18/8" stainless; it is the most versatile and most widely used stainless steel, available in a wider range of products, forms and finishes than any other. It has excellent forming and welding characteristics. The balanced austenitic structure of Grade 304 enables it to be severely deep drawn without intermediate annealing, which has made this grade dominant in the manufacture of drawn stainless parts such as sinks, hollow-ware and saucepans. For these applications it is common to use special "304DDQ" (Deep Drawing Quality) variants. Grade 304 is readily brake or roll formed into a variety of components for applications in the industrial, architectural, and transportation fields. Grade 304 also has outstanding welding characteristics. Post-weld annealing is not required when welding thin sections.

 

 

 

Corrosion Resistance

 

Excellent in a wide range of atmospheric environments and many corrosive media. Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 60°C. Considered resistant to potable water with up to about 200mg/L chlorides at ambient temperatures, reducing to about 150mg/L at 60°C.

 

Heat Resistance

 

Good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C. Continuous use of 304 in the 425-860°C range is not recommended if subsequent aqueous corrosion resistance is important. Grade 304L is more resistant to carbide precipitation and can be heated into the above temperature range.

 

Heat Treatment

 

Solution Treatment (Annealing) - Heat to 1010-1120°C and cool rapidly. These grades cannot be hardened by thermal treatment.