ASTM A295 52100 SAE 52100 Round Bearing Steel Tube , Thick Wall Stainless Steel Tubes

Delivery Time:25~35days
Certification:ISO9001 14001 BV TUV PED DNV etc

ASTM A295 52100 SAE 52100 Round Bearing Steel Tube , Thick Wall Stainless Steel Tubes

Quick Detail:

Products: ASTM A295 51100 / SAE 51100 Stainless Bearing Steel Tube
Standard: GB / SKF/ ASTM / DIN / JIS / BS 
Size(mm):

OD:8mm ~ 101.6mm

WT:1.0mm ~ 10mm

Length: Fixed(6m,9m,12,24m) or normal length(5-12m)

Description:

1. ASTM A295 52100 main features and application
ASTM A295 52100 is a kind of high-carbon chromium bearing steel. It has good synthesis performance.Quenching and tempering will make 52100 steel high and even hardness, and excellent abrasive resistance and fatigue strength. Good hot workability,after spheroidizing annealing, 52100 has good machinability, sensitive to white dot.
ASTM A295 52100 is mainly used to manufacture internal-combustion engine,electric locomotive,machine tool,tractor,steel rolling equipment,driller,steel balls,roller,and axle sleeve of rail truck, mining machine spiale.
2. The equal material of ASTM A295 52100 in different standard.

ASTM A295	GB/T18254	ΓOCT 801	ISO683-17	JIS G4805	DIN 17230	NF A35-565
52100	GCr15	IIIX15	1	SUJ2	100Cr 6	100Cr 6

ASTM A295 52100 chemical composition by %:

C	Si	Mn	Cr	Mo	P	S	others
0.95-1.05	0.15-0.35	0.25-0.45	1.4-1.65	≤0.1	≤0.025	≤0.02	Ni≤0.30 Cu≤0.25 Ni+Cu≤ 0.5

ASTM A295 52100 mechanical property and delivery condition:

Category	Standard	Delivery  Condition	Anneal (soften or spheroidizing ) hardness  HBW
Hot rolled bar	ASTM A295	Hot rolled,hot rolled soften annealing,hot rolled spheroidizing annealing,hot rolled spheroidizing annealing skin,hot rolled soften annealing skin.	179-207
Forging bar
Cold drawn bar	Cold drawn or burnishing
Hot rolled tube/pipe	Hot rolled,hot rolled annealing burnishing
Cold drawn tube/pipe	Cold drawn
Steel  wire rod	Hot rolled or spheroidizing annealing
Wire	Annealing	Quenching HRC≥62
Wire	Annealing	φ≤10mm Rm :590-760MPa Φ>10mm HBW≤229
Phosphorus cold drawn	φ≤10mm Rm :≤ 850MPa Φ>10mm HBW≤229
Cold drawn,burnishing	--
Hot rolled or Forging bar,cold drawn bar and wire	Hot rolled,cold drawn,annealing	HBW 179-207

Applications:

1,Mainly used for ma