High Performance Extruded Polystyrene Foam Board for Airport Runway

Delivery Time:10-15 days after receiving deposit.
Certification:ISO MA

Nanjing Ourgreen 500Kpa,CO2 Styrofoam Sheet, Extruded Polystyrene Foam Board for Airport Runway

Nanjing Ourgreen 500 Kpa Extruded Polystyrene Foam Board in Airport Runway Parking Area

Frost - heave causes uneven ground on roads of Highspeed Railway, Pavement and Airport, which 

was mainly invaded by Cold Weather, Moisture and Frost. Ourgreen XPS Board prevents penetration

of Moisture, decrease damage of extreme weather on road base, minimize freeze - thaw effect, and 

prolong its life so as to ensure traffic safety.

Usually a High Compression Strength of 500Kpa to 700Kpa is applied in this special field. 

Blowing Agents of Ourgreen 500Kpa Extruded Polystyrene Foam Board

The Blowing Agent of CO2 is added in the formulation in order to reach a Compression Strength of 700Kpa.

The CO2 tends to make smaller pore size and make density as high as 50Kg/m3, which enables XPS to 

bear higher Compression Strength.

The existence of CO2 presents higher System Pressure requirement to the extruder. Due to boiling point

of CO2 is as low as - 78.4 degree, the Extruding System Pressure must be kept around 25Mpa to maintain

its liquid state, which means Mould can not be opened largely. This also determines that thickness greater 

than 50mm at 700Kpa is difficult to produce.

Standard Requirements of of Ourgreen 700Kpa, Extruded Polystyrene Foam Board:

Item		Unit	Index	Standard
Apparent Density		Kg/M3	43 - 47	GB/T6343 - 1995
Thermal Conductivity	10℃            25℃	W/(m∙k)	≦ 0.035 ≦ 0.038	GB/T 10294 - 2008
Shear Strength		Kpa	≧ 300	GB/T10007 - 2008
Compression Strength		Kpa	≧ 500	GB/T 8813 - 2008
Elasticity Modulus		Mpa	38 - 42	GB/T 8813 - 2008
Closed-cell Rate		%	≧ 95	GB/T10799 - 2008
Dimensional Stability		%	≦5	GB/T8811 - 2008
Fire Behaviour			C	GB 8624 - 2008

Nanjing Ourgreen 500Kpa Extruded Polystyrene Foam Board Physical Parameters:

Items	Value	Conditions
Compression Strength	500 Kpa	Tested at 10% deflection
Thermal Conductivity	0.032 W/(m.k)	At 25 ℃
Water Absorption	0.5%	V/V
Water Vapor  Permeability	2.7 ng/(m.s.Pa)	23℃ ±1℃   RH 50%±5%
Working Temperature	-50℃ to + 75 ℃
Dimensional Stability	≦ 1.5%	70 ± 2 ℃ 48h, 90%RH
Creep	≦ 5%	80 ± 2℃  48h, 20Kpa
Fire Classification	E

Nanjing Ourgreen 500Kpa Extruded Polystyrene Foam Board Packing Details:

Thickness (mm)	Width (mm)	Length (mm)	Pcs/Pack	M2/Pack
50	600	2400	8	11.52