Granite Coating (Water-based PTFE Non-stick Coating) good quality

Product code

W800-1011P  （primer）

W800-1011M  （mid）

W800-1011T   （top）

Features

—           High hardness, excellent scratch resistance and   long-lasting non-stick performance and service life.

—           Granite effect appearance;

—           Environmental friendly water-based coating, free   from PFOA.

—             Excellent chemical resistance and abrasion   resistance;

—             In accordance with rules of FDA、LFGB、RoHS.  

Application

This series coating could be   used on inside of aluminum fry pan, wok, soup pot, rice cooker, electric high   pressure saucepan, electric saucepan, baker, etc. As for specific use, please   do complete applicability test.

Viscosity

Room temperature,

rotary viscosimeter

NK-2 Cup(mid)

600cp-800cp（primer）

200cp-500cp（mid）or

15s-30s( mid )

300cp-550cp（top）

GB/T 1723-1993

  Solid   content

380℃×10min

34.0±2.0（primer）

25.0±2.0（mid）

36.0±2.0（mid）

JIS K 6893—1995

Density

Room temperature,

gravity cup

1.30±0.20（primer） 1.10±0.20（mid）

1.30±0.20（top）

GB 6750—1986

Coverage        

Theoretical value       

10.5±2（primer）

 15.0±2（mid）

12.5±2（top）

Appearance

Visual

Grey granite effect appearance

Color             

Color of the film surface 

 Same as   standard  

    colorimetric plate

Thickness       

Thickness gauge        

25~40

GB/T 13452.2—1992

Gloss ，°             

60 ° glossmeter

5~10

GB/T 9754

Hardness     

ZHOANGHUA pencil

≥2H

GB/T 6739

Adhesion

Hatch cross test 1.5mm×1.5mm,100/100

squares,3M adhesive tape10 times.

  Grade   one

JIS K 6894—1996

Non-stick

Performance     

Fry eggs at 160±10℃  160±10℃

≥10 eggs

/

Abrasion Resistance

3KG/21cm2 pressure, 3M 7447B abrasion   pad,   change a new pad once 250   cycles, 5% detergent solution.

≥5000 cycles

BS 7069:1988

Corrosion Resistance 

Boiling in 10% salt water for 24 hours  

No blister

/

Certificates

Tested   by SGS

Meet   RoHS、FDA、LFGB   standards

/