carbon Fiber used for the Sewage and water treatment

CARTON

 carbon Fiber

1.size:STF-1300,Specific surface area more than 1200,Thickness ,3-4mm,Solvent recovery material;

2.size:STF-1600,Specific surface area more than 1400,Thickness ,3-4mm,Solvent recovery material

3.size:STF-1800,Specific surface area more than 1600,Thickness ,3-4mm,Solvent recovery material;

DETAILS:

1) The pore structure of ACF and GAC is very different, as shown in Figure 1 and Figure 2. The pore distribution of ACF is basically mono-dispersed, mainly composed of micropores less than 2.0nm, and the pore mouth is directly opened on the surface of the fiber. The diffusion path of the adsorbent to the adsorption site is short, and the fiber diameter is fine, so the contact area with the adsorbed substance is large, increasing the adsorption probability, and the contact can be uniform.

2) Large specific surface area, up to 2500㎡/g, about 5-100 times of GAC; Large adsorption capacity, about 1.5~100 times of GAC; Adsorption capacity of GAC is more than 400 times; The adsorption and desorption speed is fast, and the adsorption number of ACF to gas can reach equilibrium in 10 seconds to several minutes. 3) The pore size distribution range is narrow, most of the pore size is below 10Angstrom (1 Angstrom =1×10-10 m). The internal structure of GAC is divided into micropores, transiting pores and macropores, while the structure of ACF has only micropores and a small number of transition pores, and no macropores, and the pore size is uniform and the distribution is relatively narrow. It is 0.1~1nm, which is the reason for the good adsorption selectivity of ACF. 4) ACF not only has obvious adsorption capacity for high concentration adsorbent, but also has excellent adsorption capacity for low concentration adsorbent. For example, when the content of toluene gas is lower than 10ppm (1ppm = 1× 10-6, the same below), ACF can also adsorb toluene, while GAC must be higher than 100ppm.

5) Heat resistance, acid and alkali resistance; It has strong REDOX properties and can reduce the high-valence gold ions to the low-valence state. 6) Small volume density, small filter resistance, about 1/3 of GAC. It can adsorb the liquid substance with larger viscosity, and the power loss is small. And ACF is easy to regenerate, the process flexibility (can be made into yarn, cloth, felt and other products); These characteristics are conducive to adsorption and desorption, so that ACF has a larger adsorption capacity and faster adsorption and desorption speed for various organic compounds.

Activated carbon fiber is made of 1QQ% viscose fiber by physical process of low temperature carburization and high temperature activation

• It is an excellent high-temperature insulation material

- not only has the general properties of other types of carbon, but also

. Make the low density,

- Low thermal conductivity,

* High temperature resistance,

- Corrosion resistance,

Make electrical conductivity and a range of excellent performance.

• Suitable as adsorption material, corrosion resistant material,

• Adsorb organic gases.

• Adsorption effect is better than granular carbon and toner.